1. Laab si aad u tafatirto ujeeddada cutubkan
H13 birta dhimanwaxaa loo isticmaalaa in lagu sameeyo maydadka been abuurka ah ee leh culays sare, maydadka kulul ee la sii daayo, maydadka been abuurka ah ee saxda ah; maydadka been abuurka ah ee aluminiumka, naxaasta iyo agabkooda.

Waa soo bandhigidda birta H13 ee adkeynaysa daminta hawada ee ka timid Mareykanka. Sifooyinka iyo isticmaalkeedu waxay asal ahaan la mid yihiin kuwa birta 4Cr5MoSiV, laakiin sababtoo ah maadada vanadium ee sareysa, waxqabadkeeda heerkulka dhexe (600 digrii) ayaa ka wanaagsan birta 4Cr5MoSiV. Waa bir matalaad leh oo leh isticmaal ballaaran oo ku jira birta shaqada kulul.
2. Astaamaha
Birta dib loo dhalaaliyay ee Elektroslag, birtu waxay leedahay adkeysi sare iyo iska caabinta dildilaaca kulaylka, birtu waxay ka kooban tahay kaarboon iyo vanadium oo ka badan, iska caabin wanaagsan oo xirasho, adkeysi yar oo daciif ah, iyo iska caabin kulayl oo wanaagsan. Heerkulka sare, waxay leedahay xoog iyo adkeysi wanaagsan, iska caabin sare oo xirasho iyo adkeysi, sifooyin farsamo oo dhammaystiran oo heer sare ah iyo xasillooni iska caabin heer sare ah.
3. Halabuurka kiimikada ee birta
Birta H13 waa bir C-Cr-Mo-Si-V ah, oo si weyn looga isticmaalo adduunka. Isla mar ahaantaana, aqoonyahanno badan oo ka kala yimid dalal kala duwan ayaa sameeyay cilmi-baaris ballaaran waxayna sahaminayaan horumarinta isku-dhafka kiimikada. Birta si weyn ayaa loo isticmaalaa waxayna leedahay astaamo aad u fiican, oo inta badan lagu go'aamiyo isku-dhafka kiimikada ee birta. Dabcan, walxaha wasakhda ah ee birta waa in la dhimaa. Xogta qaar ayaa muujineysa in marka Rm uu yahay 1550MPa, isku-dhafka sulfur ee maaddada laga dhimo 0.005% ilaa 0.003%, taasoo kordhin doonta adkeysiga saameynta qiyaastii 13J. Sida iska cad, heerka NADCA 207-2003 wuxuu dhigayaa in isku-dhafka sulfur ee birta H13 ee heerka sare ah uu ka yar yahay 0.005%, halka isku-dhafka sulfur ee heerka sare uu ka yar yahay 0.003% S iyo 0.015% P. Halabuurka birta H13 ayaa lagu falanqeeyay hoos.

Kaarboon: American AISI H13, UNS T20813, ASTM (nooca ugu dambeeyay) H13 iyo FED QQ-T-570 H13 bir ah waxay leeyihiin kaarboon ka kooban (0.32 ~ 0.45)%, taas oo ah kaarboonka ugu badan ee dhammaanBiraha H13Ballaaran. Kaarboonka ku jira Jarmalka X40CrMoV5-1 iyo 1.2344 waa (0.37~0.43)%, heerka kaarboonkuna waa cidhiidhi. DIN17350 Jarmalka, kaarboonka ku jira X38CrMoV5-1 waa (0.36~0.42)%. Kaarboonka ku jira SKD 61 ee Japan waa (0.32~0.42)%. Kaarboonka ku jira 4Cr5MoSiV1 iyo SM4Cr5MoSiV1 ee GB/T 1299 iyo YB/T 094 ee dalkayga waa (0.32~0.42)% iyo (0.32~0.45)%, kuwaas oo la mid ah SKD61 iyo AISI H13, siday u kala horreeyaan. Gaar ahaan, waa in la tilmaamaa in kaarboonka ku jira birta H13 ee ku jirta Ururka Kaarboonka ee Waqooyiga Ameerika ee NADCA 207-90, 207-97 iyo 207-2003 lagu qeexay (0.37~0.42)%.

Birta H13 oo ka kooban 5% Cr waa inay lahaataa adkeysi sare, sidaa darteed maaddada C waa in lagu hayaa heer sameeya xaddi yar oo isku-dhafan oo ah isku-darka C ee isku-dhafka ah. Woodyatt iyo Krauss waxay tilmaameen in jaantuska wejiga ternary ee Fe-Cr-C ee 870℃, booska birta H13 uu ka fiican yahay isgoyska gobollada saddex-geesoodka ah ee austenite A iyo (A+M3C+M7C3). Tirada C ee u dhiganta waa qiyaastii 0.4%. Jaantusku wuxuu sidoo kale calaamadeeyay kororka xaddiga C ama Cr si loo kordhiyo xaddiga M7C3, iyo birta A2 iyo D2 oo leh iska caabin sare oo xirasho ah si loo barbardhigo. Waxa kale oo muhiim ah in la ilaaliyo heerka C ee hooseeya si looga dhigo barta Ms ee birta inay qaadato heer heerkul oo aad u sarreeya (birta Ms ee H13 guud ahaan waxaa lagu qeexaa 340℃), si birta loo damiyo heerkulka qolka. Soo hel qaab-dhismeedka isku-dhafka ah ee isku-dhafka ah ee C oo inta badan ka kooban martensite iyo qadar yar oo ah haraadiga A iyo qaybinta isku-dhafka ah ee haraadiga ah, oo hel qaab-dhismeedka martensite ee isku-dhafka ah ee isku-dhafka ah ka dib marka la kululeeyo. Ka fogow inaad beddesho austenite-ka aadka u badan ee la hayo heerkulka shaqada si ay u saamayso waxqabadka shaqada ama isbeddelka shaqada. Qadarkan yar ee austenite-ka la hayo waa in si buuxda loogu beddelaa labada ama saddexda hab-raac ee lagu kululeeyo ka dib marka la damiyo. Jid ahaan, waxaa halkan lagu tilmaamay in qaab-dhismeedka martensite-ka ee la helay ka dib markii la damiyo birta H13 uu yahay lath M + qadar yar oo ah jajab M + qadar yar oo ah haraadiga A. Karbohaydraytyada aadka u fiican ayaa ku soo daatay lath M ka dib markii la kululeeyo. Aqoonyahannada gudaha ayaa sidoo kale sameeyay shaqo qaar.